A brass wire 2 m long at 27^@C is held t...

A brass wire 2 m long at `27^@C` is held taut with negligible tension between two rigid supports. If the wire is cooled to a temperature of `-33^@C`, then the tension developed in the wire, its diameter being 2 mm, will be (coefficient of linear expansion of brass`=2.0xx10^(-5)//^(@)C` and Young's modulus of brass `=0.91xx10^(11)Pa`)

Promotional Banner

Similar Questions

Explore conceptually related problems

A brass wire 1.8 m long at 27^(@)C is held taut with little tension between two rigid supports. If the wire cooled to a temperature of -39^(@)C , what is the tension developed in the wire, if its diameter is 2.0 mm ? Coefficient of linear expansion of brass = 2.0 xx 10^(-5)//^(@)C , Young's modulus of brass = 0.91 xx 10^(11) Pa .

A brass wire 1.8 m long at 27^(@)C is held taut with little tension between two rigid supports. If the wire cooled to a temperature of -39^(@)C , what is the tension developed in the wire, if its diameter is 2.0 mm ? Coefficient of linear expansion of brass = 2.0 xx 10^(-5)//^(@)C , Young's modulus of brass = 0.91 xx 10^(11) Pa .

A brass wire 1.8 m long at 27^@C is held when taut with little tension between two rigid supports. If the wire is cooled to a temperature - 39^@C , what is the tension developed in the wire, if tis diameter is 2.0 mm? Coefficient of linar expansion of brass = 2.0 xx 10^5 ^@C^-1 , Young's modulus of brass = 0.91 xx 10^11 Pa .

A brass wire 1.8 m long at 27 ^(@) C is held taut with little tension between two rigid supports. If the wire is cooled to a temperature of - 39 ^(@) C . what is the tension developed in the wire, if its diameter is 2.0 mm ? Co-efficient of tear expansion of brass = 2.0 xx 10^(-5) K^(-1) , Young's modulus of brass = 0.91 xx 10^(11) Pa.

A brass wire 1.8 m long at 27 ^(@) C is held taut with little tension between two rigid supports. If the wire is cooled to a temperature of - 39 ^(@) C . what is the tension developed in the wire, if its diameter is 2.0 mm ? Co-efficient of tear expansion of brass = 2.0 xx 10^(-5) K^(-1) , Young's modulus of brass = 0.91 xx 10^(11) Pa.

A brass wire 1.8 m long at 27 ^(@) C is held taut with little tension between two rigid supports. If the wire is cooled to a temperature of - 39 ^(@) C . what is the tension developed in the wire, if its diameter is 2.0 mm ? Co-efficient of tear expansion of brass = 2.0 xx 10^(-5) K^(-1) , Young's modulus of brass = 0.91 xx 10^(11) Pa.